GR 1221 / GR 468
Kyoritsu Adhesives
Kyoritsu Chemical & Co., Ltd. manufactures adhesives used in optical communication devices.
Kyoritsu Chemical & Co., Ltd. manufactures adhesives that are used in a variety of optical devices for highly accurate component attachment. The adhesives have desirable attributes, such as high glass transition temperature and low moisture absorption, making it ideal for fixing components that require high accuracy. The adhesives can be used, for example, to fix fibers in V-groove arrays, or Fiber Bragg Gratings to substrate/fibers.
Hitachi High Technologies America is Kyoritsu Chemical & Co., Ltd.'s sales and marketing representative for North America.
Advantages:
- High hardness
- High Tg (glass transition temperature)
- Low water absorption/low moisture absorption
- Low curing shrinkage
- Low outgas
- Humidity/solvent durability
- You can choose either UV or Heat curing
Applications:
- Optical Communication Devices
- Optical Pick Up
- Semiconductor Package & Devices
- Liquid Crystal Display
- Flat Panel Display
- Projector
| Coupler, FBG (Fiber Bragg Grating) |
| | W/R No. 8700-7 H | W/R No. 8774 | W/R No. x-8700-7K5 |
| Main Materials |
Epoxy |
Epoxy |
Epoxy |
| Appearance |
White |
Light Grey |
White |
| Viscosity |
55,000 mPa-s |
40,000 mPa-s |
75,000 mPa-s |
| UV Cure |
6,000 mJ/cm sq. |
6,000 mj/cm sq. |
3000 ~ 6000 mJ/cm sq. |
| Heat Anneal |
120 C x 10 min
100 C x 30 min
|
120 C x 10 min
100 C x 30 min
|
120 C x 10 min
100 C x 30 min
|
| Heat Cure |
120 C x 1 hr |
120 C x 1 hr |
|
| Hardness |
85
Type D
|
88
Type D
|
87
Type D
|
| Curing Shrinkage |
3.00% |
0.76% |
2.00% |
Water Absorption
Rate
|
1.10% |
|
|
Moisture
Absorption Rate
|
1.48% |
|
1.40% |
Water Vapor
Permeability
|
|
|
11.7 g / m2
(24 hr) & 85 C/85%
|
| |
|
5.8 g / m2
(24 hr) & 65 C/95%
|
| Tg |
132.6 C |
158.3 C |
132.0 C |
| CTE: a1 |
5.3 x 10-5 |
5.3 x 10-5 |
5.3 x 10-5 |
| CTE: a2 |
5.3 x 10-5 |
5.3 x 10-5 |
5.3 x 10-5 |
| Shelf Life |
3 Months |
2 Months |
2 Months |
| (Dark & Cold Place) |
Refrigerator |
25 +/- 5 C
(Dark Place)
|
| Application |
FBG Coupler |
FBG Coupler |
FBG Coupler |
| Fiber Array |
| | W/R No. XOC-03H2 | W/R No. XOC-03HS1 | W/R No. XVL-14 |
| Viscosity |
1800 mPa-s |
3800 mPa-s |
12000 mPa-s |
| UV Cure |
6,000 mJ/cm sq. |
3,000 mj/cm sq. |
3000 ~ 4500 mJ/cm sq. |
| Heat Cure |
120 C x 1 hr |
120 C x 1 hr |
|
| Hardness |
86
Type D
|
86
Type D
|
30 +/- 5
Type A
|
| Curing Shrinkage |
1.90% |
1.80% |
4.80% |
Moisture
Absorption Rate
|
|
|
41 g / cm2 (24 hr) |
| (PCT 20 hrs) |
1.20% |
|
|
| Tg |
127 C |
146 C |
146 C |
| CTE: a1 |
6.7 x 10-5 |
6.9 x 10-5 |
|
| CTE: a2 |
2.1 x 10-4 |
1.8 x 10-4 |
|
Adhesive
Strength
|
|
|
|
| Shear |
17.9 Mpa |
|
|
| T-Peel Strength |
3.63 N/mm |
4.80 N/mm |
4.80 N/mm |
| Application |
FIBER ARRAY
Fixing
|
FIBER ARRAY
Fixing
|
FIBER ARRAY
Potting
|
Telcordia Testing
| GR 1221 |
| Test Type | Test Condition | Test Pass or Fail |
| Dry Heat |
85 C @ 2000 hrs |
Pass |
| Damp Heat Test |
85 C /85% RH @ 2000 hrs |
Pass |
| Temperature Cycle |
-40 C ~ 80 C @ 2000 hrs
1 cyc. 8 hrs 1000 hrs
|
Pass |
| GR 468 |
| Test Type | Test Condition | Test Pass or Fail |
| Accelerated Aging |
85 C @ 2000 hrs |
Pass |
| Damp Heat Test |
85 C /85% RH @ 2000 hrs |
Pass |
| Temperature Cycle |
-40 C ~ 80 C @ 2000 hrs |
Pass |
| Popcorn Test |
After; -40 C ~ 85 C @ 200 hrs
After; 85 C/85% @ 72 hrs, Put into
Solder (260 C) @ 10sec
|
Pass |